| PROPERTIES | UNIT | ASTM TEST METHOD | PTFE | |
| PHYSICAL | Melting Point | °C | – | 327 |
| specific Gravity | – | D792 | 2.14-2.20 | |
| MECHANICAL | Tensile Strength | Mpa { kgf/cm² } | D638 | 13.7-34.3 {140-350} |
| Elongation | % | D638 | 200-400 | |
| Compresive Strength | Mpa { kgf/cm² } | D695 | 11.8 {120} | |
| Impact Strength (Aizot) | J/m { kgf°cm/cm} | D526A | 160 { 16.3} | |
| Hardness (Rockwell) | – | D785 | – | |
| Hardness (Shore) | – | D2240 | D50-55 | |
| Bending elascity | GPA { 10³kgf/cm²} | D790 | 0.55 {5.6} | |
| Tensile Strength | GPA { 10³kgf/cm²} | D638 | 0.40-0.55 {4.1-5.6} | |
| Coeffcient of Dynamic friction | – | 0.69MPa {7kgf/cm³} | 0.10 | |
| 3m/min | ||||
| THERMAL | Thermalconductivity | W/(m°K) | C177 | 0.25 |
| {Kcal/(m·hr·°C)} | {0.22} | |||
| Specific Heat | J/(°C·g) {cal/(°C·g) | – | 1.05 {0.25} | |
| Coeffcient of Linear expansion | 10¯⁵/°C | D696 | 10 | |
| Ball Pressure | °C | – | 180 | |
| Max.Service Temperature | °C | Unloaded | 260 | |
| Temperature thermal deformation ratio | ||||
| 1.81 Mpa{18.5kgf/cm²} | °C | – | 121 | |
| 0.45 Mpa{4.6kgf/cm²} | °C | – | 121 | |
| ELECTRICAL | Volumetric resistance ratio | °cm | D257 (50%.RH.235) | >10¹⁸ |
| Dielectric breakdown strength (Short term) | MV/m | D149 | 19 | |
| Kv/MM (3.2mm thickness | ||||
| Dielectric constant | ||||
| 60Hz | pF/m | D150 | <18.6 {<2.1} | |
| 10³Hz | pF/m | D150 | <18.6 {<2.1} | |
| 10⁶Hz | pF/m | D150 | <18.6 {<2.1} | |
| Anti arcing property | sec | D495 | >300 | |
| Dielectric dissipation factor | ||||
| 60Hz | – | D150 | <0.0002 | |
| 10³Hz | – | D150 | <0.0002 | |
| 10⁶Hz | – | D150 | <0.0002 | |
| DURABILITY | Water absorption (24h) | % | D570 | 0.00 |
| 3.2mm thickness combustibility | – | (UL/94) | V-0 | |
| Oxygen index | – | D2863 | >95 | |
| Effect of direct sunlight | – | – | NO | |
| Effect of weak acid | – | D543 | NO | |
| Effect of strong acid | – | D543 | NO | |
| Effect of weak alkali | – | D543 | NO | |
| Effect of strong alkali | – | D543 | NO | |
| Effect of solvent alkali | – | – | NO |
Looking for high-quality Teflon PTFE rods and sheets in Malaysia? Look no further! Teflon known as PTFE that are perfect for various applications.
Teflon PTFE Rods
Teflon PTFE rods are known for their exceptional corrosion resistance and ability to withstand high temperatures. Whether you’re in the chemical industry, food processing, medical device manufacturing, these rod will meet your needs. They are highly favored in the Malaysian market for their reliable quality and excellent performance.
Teflon PTFE Sheets
Similarly, Teflon PTFE sheets are highly sought after in Malaysia for their outstanding chemical resistance and electrical insulation properties. Any electronics industry, pharmaceutical sector, and beyond. They offer reliable quality and exceptional performance, ensuring your satisfaction.
Application examples
Polytetrafluoroethylene sheets and rod find application in a multitude of industries for diverse reasons, such as:
- Chemical engineering part
- Electronic and electrical
- Food industries
- Gaskets
- Semiconductor
- Valves Gaskets
Invest in Trusted Quality
Teflon PTFE Rods are cylindrical shapes, while Teflon PTFE Sheets are flat, providing versatility for different applications such as gaskets, seals, bearings, and lining materials. They offer exceptional chemical resistance, low friction, and high-temperature stability. Widely used in various industries for their non-stick properties and excellent electrical insulating capabilities.
In Malaysia, these Teflon PTFE products are sought after for their durability, corrosion resistance, and suitability in demanding environments, making them essential components in many industrial processes.
With their superior properties and our commitment to excellence, you can trust our products to deliver the results you desire. Order now and experience the difference of high-quality products in Malaysia.