Titanium

We are Malaysia’s leading titanium supplier and, no matter how big or small the order, we’re here to help. We supply Titanium sheet rod and wire to other countries too.
titanium-500x500

Grade 1

GENERAL PROPERTIES METRIC ENGLISH COMMENTS
PHYSICAL PROPERTIES
Density 4.51 g/cc 0.163 lb/in³
MECHANICAL PROPERTIES
Hardness,Brinell 120 120 annealed
Hardness,Knoop 132 132 Estimated from Brinell
Hardness,Rockwell B 70 70 annealed
Hardness,Vickers 122 122 Estimated from Brinell
Tensile Strength,Ultimate 240 Mpa 34800 psi
Tensile Strength,Yield 170-310 Mpa 24700 – 45000psi
Elongation at Break 24% 24%
Reduction of Area 35% 35%
Modulus Of Elasticity 105GPa 15200ksi In Tension
Compressive Modulus 110 Gpa 16000 ksi
Poisson’s Ration 0.37 0.37
Charpy Impact 310J 229 ft-lb V-notch
Shear Modulus 45 Gpa 6530 ksi
ELECTRICAL PROPERTIES
Electrical Resistivity 4.5e-005 ohm-cm 4.5e-005 ohm-cm
THERMAL PROPERTIES
Heat of Fusion 325 J/g 140 BTU/lb High Purity Ti
CTE,linear 20°C 8.6 Ʋm/m-°C 4.78 Ʋin/in-°F 0 – 100°C
CTE,linear 250°C 9.2 Ʋm/m-°C 5.11 Ʋin/in-°F Average over the range 0-315°C
CTE,linear 500°C 9.7 Ʋm/m-°C 5.39 Ʋin/in-°F 0-540°C;CTE is higher perpendicular to the c-axis
Specific heat Capacity 0.52 J/g-°C 0.124 BTU/lb-°F Heat Capacity at 540°C IS 0.67 J/g-°C
Thermal Conductivity 16 W/m-K 111 BTU-in/hr-ft²-°F annealed
Melting Point Max 1670°C Max 3040°F Liquidus
Liquidus  1670°C  3040°F
Beta Transus 888°C 1630°F
OPTICAL PROPERTIES
Emissivity (0-1) 0.3 0.3 High Purity Ti at 710°C
Reflection Coeffcient,Visible (0-1) 0.56 0.56 High Purity Ti ;visible light

Grade 2

GENERAL PROPERTIES METRIC ENGLISH COMMENTS
PHYSICAL PROPERTIES
Density 4.51 g/cc 0.163 lb/in³
MECHANICAL PROPERTIES
Hardness,Knoop 170 170
Hardness,Rockwell B 80 80
Hardness,Vickers 145 145
Tensile Strength,Ultimate 344 Mpa 49900 psi
Tensile Strength,Yield 275-410 Mpa 39900-59500psi
Elongation at Break 20% 20%
Reduction of Area 35% 35%
Modulus Of Elasticity 105GPa 15200ksi In Tension
Compressive Modulus 110 Gpa 16000 ksi
Poisson’s Ration 0.37 0.37
Izod Impact 114-171 J 84.1 – 126 ft-lb
Fatigue Strength 300 Mpa 43500 psi 1E+7 cycles,Unnotched
Fatigue Strength 425 Mpa 61600 psi 30,000 cycles,Unnotched
Fracture Toughness 66 Mpa-m½ 60.1 ksi-in½ K(Q);annealed
Shear Modulus 45 Gpa 6530 ksi
ELECTRICAL PROPERTIES
Electrical Resistivity 5.2e-005 ohm-cm 5.2e-005 ohm-cm
THERMAL PROPERTIES
Heat of Fusion 325 J/g 140 BTU/lb High Purity Ti
CTE,linear 20°C 8.6 Ʋm/m-°C 4.78 Ʋin/in-°F 0 – 100°C
CTE,linear 250°C 9.2 Ʋm/m-°C 5.11 Ʋin/in-°F Average over the range 0-315°C
CTE,linear 500°C 9.7 Ʋm/m-°C 5.39 Ʋin/in-°F 0-540°C;CTE is higher perpendicular to the c-axis
Specific heat Capacity 0.523 J/g-°C 0.125 BTU/lb-°F Heat Capacity at 540°C IS 0.67 J/g-°C
Thermal Conductivity 16 W/m-K 114 BTU-in/hr-ft²-°F annealed
Melting Point Max 1665°C Max 3030°F Liquidus
Liquidus  1665°C  3030°F
Beta Transus 913°C 1680°F
OPTICAL PROPERTIES
Emissivity (0-1) 0.3 0.3 High Purity Ti at 710°C
Reflection Coeffcient,Visible (0-1) 0.56 0.56 High Purity Ti ;visible light